JIS G3131 Hot-roll mild steel plates, sheet and strip
JIS G3131 Hot-roll mild steel plates, sheet and strip. 1. Scope. The Japanese Industrial Standard specifies the hot-rolled mild steel plates, sheets and strip (hereafter referred to as "steel sheet and coil")intended for general fabrication purposes and drawing. Remarks 1. The standards cited in this Standard are given in Attached Table 1. 2.
JIS G 3131 Hot-rolled mild steel plates, sheet and strip ApplicationsHot-rolled mild steel plates, sheets and strips intended for general fabrication purposes and drawing • Minimum yield strength / Mindestwert der oberen Streckgrenze / Limite dТelasticite minimale • Tensile strength / Zugfestigkeit / Resistance a la traction
G 3131 SPHC,SPHD steel plate - BEBON INTERNATIONAL
JIS G3131 SPHC/SPHD steel plate/sheet is stamping and cold forming steels,SPHC,SPHD and SPHE are symbols used in the Japanese Industrial Standards for steel sheets.They are characterized by a minimum tensile strength of 270MPa. SPHC/SPHD steel Chemical composition
JIS G3131 SPHE steel plate steel,JIS G3131 SPHE steel
JIS G3131 SPHE steel plate/sheet is stamping and cold forming steels,it is suitable for non-structural press work and forming.SPHE tensile strength is around 270 MPa. (different min strength point at the different thickness.) More detailed information about JIS G3131 SPHE steel Mechanical Properties , please refer to the following table:
JIS G3132 Hot Rolled SPHT-1 Steel - Material Grades
SPHT-1 is a material grade and designation defined in JIS G 3132 standard. JIS G 3132 is a Japanese material standard for Hot Rolled steel plates, sheets, strips for pipes & tubes making. This quality of hot Rolled steel is a type of steel that is utilized in making pipes & tubes material.
SAPH440 Steel - JIS G3113 Structural Automobile Hot Rolled
Jan 27, 2013 · JIS G 3113 is a Japanese material standard that defines the specifications of hot-rolled steel plates, sheets, and strip for automobile structural uses. SAPH440 Full Form Sources say that SAPH 440 means Steel Automotive Pickled Hot-rolled and 440 MPa minimum tensile strength .
Yield point (N/mm2) Elongation (%) Test piece (JIS) Bending property Thickness (mm) Bending angle Inner radius Test piece Thinner than (JIS) 6 mm 6 mm or thicker and thinner than 8 mm 8 mm or thicker and 14 mm or thinner 1.6 or more, but less than 2.0 2.0 or more, but less than 2.5 2.5 or more, but less than 3.15 3.15 or more, but less than 4.0 4.0 or more, but
JIS G3131 SPHD steel plate steel,JIS G3131 SPHD steel
JIS G3131 SPHD steel plate/sheet is stamping and cold forming steels,it is suitable for non-structural press work and forming.SPHD tensile strength is around 270 MPa. (different min strength point at the different thickness.) More detailed information about JIS G3131 SPHD steel Mechanical Properties , please refer to the following table:
SPECIAL STEEL Company-Business:Steel plate shearing
JIS G3131. No special strength requirements of the product parts . General molding, bending, such as wire piping, bicycle parts and other gear sets. SPHD SPHE. JIS G3131. Low yield strength, high elongation rate, anti-ear extension. Complex formation or severe bending of steel pipes, multiple deep drawing for cup parts, motor housing, compressor housing, etc.
SPHC steel coil under JIS G3131 standard, it is a kind of stamping and cold forming steel. JIS G 3131 is a Japanese material standard for hot rolled steel. The commercial quality hot rolled steel is a type of steel that can be used commercially for forming purposes that can also include shearing of a metallic sheet.
COMPRARISONS FOR INDUSTRIAL STANDARDS. ISO 4950/2-81 Part 2Products supplied in the normalized or controlled rolled condition ISO 4950/3-81 JIS G 3128 High yield strength steel plates for welded structure ASTM A 514/ A 514 M-91 Spec. for high-yield strength, quenched and tempered alloy steel plate, suitable for welding
Rangkuman DiskusiBeda ASTM A36 dan JIS 3101 SS 400
Feb 02, 2011 · Sedangkan untuk JIS 3101 SS400, Tensile 400 – 510 MPa, Yield min 235 MPa dan Elongation min 21%. Kira-kira..ada gak teman yang bisa kasih masukan kapan kita pilih menggunakan ASTM A36 dan kapan kita menggunakan JIS 3101 SS400 dalam mendesign suatu project? Tanggapan 1- novembri nov . Ini ada sedikit article ttg pertanyaan Pak May..